Solid propellants of the composite type, containing separate fuel (or reducer, chemically) and oxidiser (in a separate compound) intimately mixed, replaced the simple double-base propellants to a considerable extent, especially for large non-military motors. The organic fuel material is initially in a liquid or semi-liquid form that can set to a solid (binder). Among the earliest substances used were asphalt and various synthetic rubbers. While generally not considered as composite, black powder was in fact the oldest composite propellant. Before 1940 black powder, in common use, was nearly synonymous with the words 'rocket motor' .
While working on the theory of rocket propulsion for his doctoral thesis in 1937, Frank Malina mentioned to Fritz Zwicky of Caltech some difficulties he was having in his study. Zwicky exploded with the opinion that Malina was wasting his time on an impossible subject. For, he said, Malina must realise that a rocket could not operate in space as it required the atmosphere to push against to provide thrust! By 1940 he realised that he was mistaken.
At Guggenheim Aeronautical Laboratory, California Institute of Technology (GALCIT),in 1939, one of the first objectives was to develop a solid propellant rocket unit capable of delivering a constant thrust on the order of 1000 pounds for a period of 10 to 30 seconds. As far as is known, no black powder or smokeless powder rocket had ever been constructed to meet these specifications of thrust and duration. Experts consulted by Malina, John Parsons, and Forman were very dubious about the possibility of doing so.
Preliminary experiments made by Parson and Forman with pressed solid propellant charges restricted to burn cigarette-fashion appeared to support this view. It was generally believed that the combustion chamber pressure of a restricted burning solid rocket unit would continue to rise from the moment of ignition until any combustion chamber of reasonable weight would burst. In other words, it was thought that such combustion was inherently unstable.
|Scout X1 - Scout X1 - COSPAR 1961-Delta|
11,362 bytes. 121 x 463 pixels.
The GALCIT group's mentor, Professor Theodore von Karman, in the spring of 1940, had to listen to both the opinions of the experts and to the explosions of Parson's rockets. One evening at home Von Karman wrote down four differential equations describing the operation of an ideal restricted burning motor, and asked Malina to solve them. It was found that, theoretically, a restricted burning unit would maintain a constant chamber pressure as long as the ratio of the area of the throat of the exhaust nozzle to the burning area of the propellant charge remained constant, that is, the process was stable. Experimental verification of the theory was soon obtained.
Credit: Thiokol. 1,570 bytes. 110 x 59 pixels.
Although there have been centuries of experiments with black powder rocket, and several investigators used smokeless powder and Ballistite in rockets between about 1918 and 1939, none of these rockets had the thrust and duration required for the aircraft "super-performance" applications. Parsons and Forman in 1938 built and tested a smokeless powder constant-volume combustion motor similar to the one that had been used by Goddard. They concluded after these tests that the mechanical complications of constructing an engine using successive impulses to obtain thrust durations of over 10 seconds was impractical. Upon Parson's recommendation, they concentrated their efforts on the development of a motor provided with a restricted burning powder charge that would burn at one end only at constant pressure to provide a constant thrust.
|Scout X3 - Scout X3 - COSPAR 1964-015|
8,646 bytes. 101 x 412 pixels.
Parsons started with the traditional sky rocket. This type of pyrotechnic device was propelled by a black powder charge pressed into a cardboard combustion chamber with a conical hole in its centre. The gases escaped through a rounded clay orifice. Its efficiency was very, very low, but it was reliable. The conical hole in the charge was believed to be the secret that kept the charge from burning down the sides of the container or to produce chamber pressures that would burst the container. The longest duration of thrust of this motor did not exceed about 1 second.
|Nova Martin - Nova Martin Marietta designs 1C and 14|
Credit: Lockheed Martin. 24,919 bytes. 483 x 477 pixels.
During 1939 and 1940, various mixtures based on black powder and mixtures of black powder with smokeless powder were tested in 1 in. and 3 in. diameter chambers. The charge for the 3 in. chamber was made up of 6 in. long pellets compressed at around 6,500 psi., and coated with various substances to form a solid or liquid seal between the charge and the walls of the chamber. The charge of the 1 in. chamber was pressed directly into the chamber in small increments at pressures between 7,700 and 12,000 psi. Most of the tests of these charges ended in an explosion.
|Scout X4 - Scout X4 - COSPAR 1964-084|
11,595 bytes. 105 x 427 pixels.
Mechanical causes for failures, such as burning of the charge on the surface next to the wall because of leakage, transfer of heat down the walls sufficient to ignite the sides of the charge, and cracking of the charge under combustion pressure, were suspected. However, there were those who were convinced that the combustion process of a restricted burning charge in a rocket motor was basically unstable. Only after von Karman and Malina proved the process was stable in their analysis of the characteristics of the ideal solid propellant rocket motor in the spring of 1940 was a concentrated effort was made to study the mechanical causes of failure.
Credit: Thiokol. 3,006 bytes. 110 x 89 pixels.
Hundred of tests were then made with different powder mixtures, using black powder as the basic ingredient, with various loading techniques and various motor designs. The dependence of chamber pressure on the ratio of chamber cross section area to nozzle throat area was determined for each specific powder mixture.
By the spring of 1941 the results were sufficiently encouraging to schedule flight tests of an aircraft equipped with solid propellant rockets specially designed for it. The propellant charge used in the Ercoupe motor was a type of amide black powder designated as GALCIT 27 (amide: organic compound containing carbon, hydrogen, oxygen, and nitrogen. Some examples: HCONH2, CH3CONH2, C6H13CONH2). The 2 lb. charge was pressed into the combustion chamber, which had a blotting paper liner, in 22 increments by a plunger with a conical nose shape at a pressure of 18 tons. The diameter of the charge was 1.75 in. and its length varied between 10 and 11 in. The motor was designed to deliver about 28 lb. thrust for about 12 seconds.
|TA Thor Agena B - TA Thor Agena B - COSPAR 1963-027|
16,306 bytes. 148 x 458 pixels.
Eighteen rocket motors were delivered every other day for the first tests at March Field, California, about an hour's drive from the project. During the first phase of the flight tests one motor failed explosively in a static test and one while Ercoupe was in level flight. Thereafter, 152 motors were used in succession without explosive failure. The motors were prepared by Parsons, Forman, and Fred Miller.
On August 16, 1941, Boushey made the first take-off of the Ercoupe with six JATOs firing. The first American manned flight of an aircraft propelled by rocket thrust alone was made by Boushey on August 23, 1941. The propeller of the Ercoupe was removed and 12 JATO units installed, of which only 11 functioned. The Ercoupe was pulled by a truck to a speed of about 25 m.p.h. before the JATOs were ignited. The airplane left the ground and reached an altitude of about 20 ft. This flight was not originally scheduled but the group could not resist the opportunity to make the improvised demonstration of the future possibility of rocket propulsion.
|Scout B1 - Scout B1 - COSPAR 1971-071|
12,300 bytes. 106 x 415 pixels.
Frank Malina noted that it was most fortunate that the flight tests were carried out close to the location of the project, which permitted the rocket motors to be fired within a few days from the time they were charged with propellant. Following the flight tests, it was found that after the motors were exposed to simulated storage and temperature conditions over several days they exploded in most cases. It was evident that either the blotting paper liner or the mechanical characteristics of the propellant were unsatisfactory.
Credit: Aerojet. 22,183 bytes. 278 x 325 pixels.
But the Navy Department regarded the successful Ercoupe tests with much interest from the point of view of application of rockets for assisted take-off of aircraft from aircraft carriers. Upon the urging of Lt. C.F. Fischer of the Bureau of Aeronautics, who had witnessed the tests, a contract was placed by the Navy with the Project in early 1942 for the development of a 200 lb. thrust, 8 second unit. The unit was designated by the acronym JATO for Jet Assisted Take-Off (sometime RATO), and this designation is still used.
|Titan 3C - Titan 3C - COSPAR 1966-099|
13,619 bytes. 117 x 443 pixels.
This Navy contract came in the midst of the explosive failure of the JATO unit developed for the Ercoupe tests. All efforts to improve the amide-black powder propellant and loading techniques of the motor developed for Ercoupe tests failed to meet specified storage conditions ranging from Alaska to Africa. Investigations of motors using Ballistite also proved negative, mainly because of its ambient temperature sensitivity (variation of its rate of burning and thrust with ambient temperature).
Thus, the spring of 1942 was one of desperation for those concerned with development of a reliable solid propellant JATO unit. They knew that theoretically it was possible to construct such an engine, but no one came forward with a promising idea until June, when Parsons, no doubt after communing with his poetic spirits, suggested trying a radical new propellant. It would consist of potassium perchlorate (KClO4- in place of potassium nitrate KNO3: saltpetre), as oxidiser, common asphalt as used on roads as a binder and fuel. These could be cast, after being mixed, into a combustion chamber.
|Scout A - Scout A - COSPAR 1967-042|
9,437 bytes. 107 x 414 pixels.
A test of the propellant, designated GALCIT 53, was quickly made and the results were so promising that work on other propellant types was dropped for a long time. Parsons was assisted in the development of the asphalt base propellant by Mills and Fred Miller. After due study of the origin of the ideas for the new propellant, Parsons was recognised as its inventor and a patent was granted in his name.
At first, the Ordnance Department objected strongly to the use of potassium perchlorate as an oxidiser because it had proved unsafe in the past. Parsons realised that their objection was no longer valid, since way had been found to produce the material with a minimum purity of 99%. Impurities in the form of dangerous chlorates (KClO3) had been practically eliminated. Sodium and potassium chlorates were used with dinitrotoluen in explosives (know as cheddites in French), also with perchlorates and various hydrocarbons-vaseline-,castor oil, and nitro. Potassium chlorate was also used as oxidiser in matches with phosphorus sesquisulfide P4S3 or tetraphosphorus trisulfide as the active fuel.
|LT Thor Agena D - LT Thor Agena D - COSPAR 1969-051|
17,222 bytes. 139 x 466 pixels.
The ruling of the Ordnance Department was thereafter changed, allowing the use of this kind of solid oxidiser. The Navy contract for 100 JATO units delivering 200 lb. thrust for 8 seconds was successfully completed, with GALCIT 53 as the propellant. Production of service-type units for the Navy began shortly thereafter at the Aerojet Engineering Corporation (organised at the end of 1941 and formally incorporated on March 19, 1942 with the GALCIT members Von Karman, Malina, Haley, Parsons, Forman, and Summerfield).
The project carried out extensive studies on asphalt-base propellants in the following years. A detailed report released in May 1944 on the propellant GALCIT 61-C by Mills give the following composition: 76% potassium perchlorate and 24% fuel. The fuel component was 70% Texaco No. 18 asphalt and 30% Union Oil Company Pure Penn SAE No. 10 lubricating oil. The fuel was liquefied at about 275°F, the pulverised potassium perchlorate added to it, and the mixture thoroughly stirred. The mixture was then poured into the combustion chamber, which had been previously lined with a material similar to the fuel component, and allowed to cool and become hard. This propellant, when burned at a chamber pressure of 2,000 psi., had a chamber temperature of 3,000-3,500°F, a specific impulse of 186, and an exhaust velocity of about 5,900 ft. per sec. Storage temperature limits were from -9 deg F to 120 deg F. GALCIT 61-C was developed in 1943 and used in service JATO units by the Navy until the end of World War II. The propellant is also used on the Private A and F research rockets.
Credit: Thiokol. 2,028 bytes. 110 x 88 pixels.
Solid propellants utilising potassium perchlorate as oxidiser produced dense clouds of white smoke (potassium chloride-KCl, like sodium chloride-NaCl, common salt), which the Navy did not like at all. Some months after GALCIT 53 was developed, Parsons informed the Project weekly research conference that he had eliminated the smoke problem by replacing potassium perchlorate with ammonium perchlorate (NH4ClO4). Navy rocket experts were immediately invited to visit the Project for a demonstration:
|Delta N6 no. 81 - Delta N6 no. 81 - COSPAR 1970-106|
11,461 bytes. 100 x 399 pixels.
"When they arrived we posted ourselves some distance from the test pit, the red flag was run up, and Parsons gave the order for his latest creation to be fired. We beheld a big cloud of with smoke and Parsons with a look of surprise on his face. He sheepishly explained that the smoke must have been caused by the humidity, for the air had been very dry on the days they had made tests before".
Ammonium perchlorate does reduce the amount of smoke produced if the air is dry, but it produces undesirable chloride in the jet. In fact Cl and H in NH4ClO4 may combine to form HCl, hydrogen chloride or hydrochloric acid with water. But that is the base of modern composite propellants.
|Diamant BP.4 - Diamant BP.4 - COSPAR 1975-039|
21,392 bytes. 123 x 453 pixels.
The project also studied the possible use of other fuels instead of asphalt, such as Napalm (sodium palmitate = NaPalm - first tried as a high temperature, high energy propellant), gelled hydrocarbons, gelled wax mixtures, and butyl rubber. A continuation of studies of the last material later led Charles Bartley, under the JPL-ORDCIT Project in 1945, to the discovery of the advantages of the castable elastomeric (polysulfide rubber) material called Thiokol. This discovery became the basis of solid propellant manufacture by the Thiokol Chemical Corporation. The Air Force Material Command terminated work by the Project on solid propellant motors on June 30, 1944. The Ordnance Department, however, continued the work for long range missile applications.
|Mu-3C - Mu-3C - COSPAR 1975-014|
13,108 bytes. 171 x 376 pixels.
During the course of this research, engineers were provided with methods of motor component design when the following characteristics of the propellant to be used were known:
The great progress made in the scientific design of solid propellant rocket motors in comparison with the empirical, traditional, method used in previous centuries can be appreciated by reference to the text "Jet Propulsion" prepared for the course at Caltech at the request of the Air Technical Service Command in 1943 and continued in the following years. The debate on the superiority of solid vs. liquid propellant rocket engines for boosters of space vehicles still rages today (but environmental considerations now favour liquid propellants).
- Sensitivity of the propellant to ambient temperature during combustion.
- Combustion pressure limit below which the propellant burns in irregular manner.
- Combustion pressure limit above which the propellant burns in an unpredictable manner.
- Storage characteristics of the propellant charge from the point of view of minimum and maximum ambient temperatures allowed and possible decomposition of the propellant with prolonged storage.
- Ignition temperature of the propellant.
- Rate of burning of the propellant as function of the combustion pressure.
- Performance characteristics of the propellant to produce rocket thrust.
|Titan 3D - Titan 3D - COSPAR 1978-060|
20,041 bytes. 153 x 507 pixels.
Sponsorship of solid-propellant research was taken over by the ORDCIT Project from the Air Force Materiel Command on July 1, 1944. By this time, JPL had made the following fundamental contributions to the design and construction of long-duration solid-propellant engines:
After the successful JATO development with the asphalt- perchlorate propellant in 1942, Mills sought a fuel-binder for the perchlorate superior to asphalt. In 1944, Charles Bartley joined Mills' group, and in 1945 introduced as a replacement for asphalt a castable elastomeric material, polysulfide rubber, produced by Thiokol Chemical Corporation. The polysulfide rubber, compared to asphalt, produced a propellant much better both as regards storage temperature limits and hardness at high atmospheric temperatures. The latter property was especially important in the design of high-thrust engines requiring a charge with an internal-burning surface rather than a cigarette-burning surface.
- Theory: Von Karman-Malina theory of constant-thrust long- duration engines (1940)
- Propellant development:
- Parsons' break-away from Ballistite with amide black powder (1940)
- Parsons' introduction of perchlorates as an oxidiser (1942).
- Parsons' introduction of asphalt as fuel-binder with perchlorates; the invention of a castable case- bonded composite propellant charge (1942).
|Scout D1 - Scout D1 - COSPAR 1979-047|
12,593 bytes. 127 x 442 pixels.
- Engine component design
- Parsons' design of a restricted-burning (case- bounded) propellant charge with amine black powder (1940).
- Malina-Mills design of a safety pressure relief valve (1942).
- Mills' review of various types of burning surfaces of a charge and theoretical confirmation that the surface of a cigarette-type burning charge was stable (1943).
Credit: Thiokol. 1,708 bytes. 110 x 64 pixels.
Since at this time only Aerojet in the USA was producing composite solid-propellant engines, that company's attention was drawn to the asphalt replacement, but it was already interested in a similar material made by the General Tire and Rubber Co. It was only at the urging of the Ordnance Department that the Thiokol Chemical Corp. entered the field of composite solid propellants with the new fuel-binder discovered at JPL.
After obtaining the experience with the composite solid- propellant missiles Private A and F, studies began at JPL in 1946 on larger missiles using, in particular, the polysulfide rubber-perchlorate type propellant. The results of these studies led eventually to the design of the tactical guided missile, Sergeant.
|Titan 3E - Titan 3E - COSPAR 1976-003|
18,177 bytes. 120 x 504 pixels.
The laboratory followed closely development with other type of solid propellants, especially Ballistite, used in high-thrust short-duration engines suitable for boosters (Aerojet built some double-base boosters using this material).
Other special-purpose rocket vehicles supported research in solid propellants and high-acceleration, and high-speed dynamics. A small vehicle unofficially called "Thunderbird" demonstrated the polysulfide composite-propellant, internal-burning star-grain solid motor in 1947. With an acceleration of over 100 G, (a precursor of the Sprint missile) it led to the Wac-scale solid-propellant research vehicle called Sergeant in 1948.
This Sergeant sounding rocket, unrelated to the tactical missile of the same name, proved to be ahead of its time. It was inspired by calculations that indicated a solid-propellant rocket of the internal-burning-star design could deliver several times the payload of a liquid-propelled V-2 type of similar weight. The motor chamber walls were very thin because the propellant, burning from within, would help contain heat and pressure.
An autopilot design effort was begun, and static tests of the motor, weighing 1300 lbs and delivering about 6000 lbs thrust for more than 30 seconds, were conducted.
Credit: Thiokol. 1,316 bytes. 110 x 36 pixels.
Difficulties with this solid rocket, manifested in the rupture of the thin-wall case, coincided with a change in the JPL mission and an acceleration and expansion of Corporal development. The Sergeant project was suspended. The electronic autopilot was adopted for the Corporal missile while the solid-propellant engineers took their problems back to the laboratory and test stand for more investigation. Further development was undertaken by the Thiokol Chemical Corporation. The ultimate heritage of this early "Sergeant" powerplant was the reliable solid rocket, used in large scale in the Sergeant and other military missiles, and in clustered miniatures to launch the first Explorer satellites.
|Scout E1 - Scout E1 - COSPAR 1974-040|
9,245 bytes. 115 x 461 pixels.
The motor evolved from the Sergeant test vehicle of 1948-49 via the Hermes RV-A-10 flight tested in March 1953. A Hermes A-2 Thiokol motor was ground tested in December 1951. The Hermes A-2 program was ended in October 1952.
The Sergeant missile was not the only result of the Thiokol polysulfide motor. Another major development was the Nike-Hercules sustainer motor (or stage two), the Lacrosse motor, and later the Bomarc B motor. Many small missiles, sounding rocket motors, and the Mercury and Gemini retro-rockets used the same propellant.
Credit: NASA. 27,800 bytes. 384 x 488 pixels.
However, the use of polysulfide by Thiokol probably caused their loss of the key Polaris contract. Aerojet won the contract with the use of a more energetic polyurethane propellant.
After that Thiokol began the use of polybutadiene for big motors and won the contract for the Minuteman first stage motor. That lead as well to the Nike-Zeus, Pershing, Castor motors, Surveyor retro (first of a series of upper stage motors) and finally to the Shuttle SRB's.
Meanwhile, Hercules began the use of double-base propellant as fuel in composite propellants, since double-based motors burned with excess of fuel. The use of a separate oxidiser also permitted the addition of energetic fuels such as aluminium powder.
Credit: Thiokol. 2,415 bytes. 110 x 108 pixels.
The excess of fuel in pure double-base caused a long afterburning flame, essentially of burning carbon (see launch-photographs of Nike Ajax and Hercules, Honest John, Terrier, and Talos). The unburned carbon cause also the dark exhaust before the afterburning.
The Hercules' Minuteman third stage was a follow-on of the Vanguard third stage.
Some composite propellants continue to use saltpetre (potassium nitrate) or ammonium nitrate.
Some composite propellant formulations and characteristics:
5,878 bytes. 67 x 364 pixels.
- Molded composite: potassium nitrate(20-50%), elastomer(10%), ammonium picrate-NH4C6H2NO7-(70-40%). Specific impulse s.l.: 160 to 200 sec. Abundant smoke. Hard to brittle.
- Castable composite: ammonium nitrate(80%), elastomer (18%), catalyst(2%). Specific impulse s.l.: 185 to 198 sec. Little smoke. Soft and resilient to hard and tough.
- Castable composite: ammonium perchlorate(50-85%), elastomer(50-15%). Specific impulse s.l.: 175 to 240 sec. Much smoke at low oxidiser; little at high oxidiser; mist at relative humidity greater than 80%. Soft and resilient to hard and tough.
|Scout G1 - Scout G1 - COSPAR 1993-041|
13,880 bytes. 108 x 387 pixels.
- Castable composite: potassium perchlorate(50-80%), elastomer(50-20%). Specific impulse s.l.: 165 to 210 sec. Abundant smoke. Soft and resilient to hard and tough.
Ammonium perchlorate is the most widely used today. It is characterised by high heat, is a good gas producer (not a smoke producer), percent of oxygen by weigh: 34 percent, specific gravity: 1.9.
Potassium perchlorate is used for fast burning rates. It is characterised by high heat, is a low gas producer, percent of oxygen by weight: 46 percent, specific gravity: 2.5.
Credit: NASA. 31,198 bytes. 403 x 485 pixels.
Ammonium nitrate is used for slower burning rates. It is characterised by low heat, is a high gas producer, and is good for gas generator propellants. It requires a greater amount of binder (fuel) to make castable, but too much binder produces excessive smoke. Ammonium nitrate's percent of oxygen by weight: 20 percent, specific gravity: 1.9. It may be the oxidiser for the future. It contains no toxic elements and no solid elements, produces no solids by decomposition, and therefore, together with a high energy non-polluting fuel, could provide a more 'environmentally friendly' solid propellant.
Credit: NASA. 13,327 bytes. 279 x 441 pixels.
Lithium perchlorate, a proposed oxidiser, is very hygroscopic and may be used in some high-temperature propellants. Percent of oxygen by weight: 60 percent, specific gravity:2.4.
The original composite propellants, used in JATO units, contained an asphalt binder. Since asphalt-perchlorate composites had poor performance and formulation characteristics, extensive research and development work was directed toward their improvement. This soon led to the discovery and acceptance of new and better chemical binder-fuels, primarily synthetic rubbers Initially, polysulfide liquid polymers were developed with only physical properties that were an improvement over those of asphalt. Later, with certain chemical-structure modifications, the overall performance of polysulfide soon outshone that of asphalt. Polysulphides, however, had a major drawback in that they released water during combustion; which interfered with efficient burning. The water by-product also limited the type of additives that could be mixed with the propellant, since water was highly reactive with materials such as aluminium. In the search for binder-fuels without the drawbacks of asphalt and polysulfides, polyurethanes (synthetic thermosetting or thermoplastic polymers) were found to have good performance and physical properties. With these aluminium could be incorporated for higher specific impulse. However, polyurethanes were so viscous that the amount of oxidisers and other solid additives that could be incorporated was limited. Eventually polybutadiene- based propellants were developed that had physical properties superior to those of polyurethanes.
Polysulfide was the first binder elastomer fuel. For rocket applications a low-molecular-weight polymer was made from dichlorodiethyl formal; sodium polysulfide was used as the liquid binder. When the mixture was heated with an appropriate curing agent such as zinc oxide, the links between adjacent polymer chains were joined together to form the rubber network. The resulting binder had a glass-transition temperature near -60°F., making it usable to about -40°F. This was a distinct advantage over the first composites.
Credit: Thiokol. 1,944 bytes. 110 x 66 pixels.
An undesirable quality of the polysulfides was the presence of sulphur atoms in the system. They produced high-molecular-weight exhaust products (sulphur dioxide with a molecular weight of 64) thereby lowering specific impulse. Since a large amount of oxidiser had to be mixed with the binder to obtain the high energy desired, the binder lost much of its rubber-like quality.
There were many organic and inorganic materials that acted as oxidisers and could be used to cure liquid polysulfide polymers. Each had its advantages and disadvantages.
|Ariane 3 V19 - Ariane 3 V19 - COSPAR 1987-078|
16,047 bytes. 113 x 436 pixels.
Thiokol developed many varieties of polysulfides with improved qualities.
Polyurethanes were the second elastomer fuel binder. The group of polymers known as polyurethanes were made by combining polyols with isocianates. The versatility in polymer chemistry was such that a large number of starting materials having varying molecular weights were available.
Compared with the polysulfides, the average molecular weight of the polyurethanes' exhaust gases was lower. This was because the polyurethanes contained only carbon, hydrogen, oxygen, and nitrogen atoms (not sulphur). An additional benefit was claimed in the processing: the backbone polymer contained substantial amounts of oxygen. It was not necessary therefore to use as great a percentage of oxidiser in the formulation of the propellant to achieve comparable energies. The increased proportion of binder to oxidiser provides added elongation and other good mechanical properties to the propellant, permitting the addition of other energetic fuels (for example aluminium).
|Nasda H-1 - Nasda H-1 - COSPAR 1987-070|
18,493 bytes. 184 x 402 pixels.
From the logistics standpoint, the starting ingredients for manufacturing polyurethane were available from a large number of chemical suppliers, whereas the liquid polysulfide rubbers were manufactured almost exclusively by a single company. This had its effect on cost, quality, and delivery time.
One of the advantages of polyurethane was that a high concentration of nitrate ester could be incorporated in the binder to give increased energy. A commonly used polyurethane binder material was ESTANE, a product of B.F. Goodrich Chemical Company.
|ASLV - ASLV - COSPAR 1992-028|
11,834 bytes. 109 x 406 pixels.
Polybutadiene Acrylic Acid.
Almost concurrently with the evolution of the polyurethane propellants, a new type of binder based on long-chained polybutadiene backbone gained the attention of rocket manufacturers. The selection of polybutadiene binder for propellants to be used over wide temperature ranges was a natural one, since most butabiene copolymers (butadiene-styrene, butadiene-acrylonitrile, butadiene- methylvinyl pyridine) had glass-transition temperatures near or below -100°F. This was advantageous, since the mechanical behaviour of a propellant during periods of strain was related to its properties at different temperatures. For example, the ability of a propellant to withstand high strain rates such as those encountered on ignition of a large-diameter rocket motor was directly related to low-temperature properties such as elongation and brittle point. Therefore, the polybutadiene propellants were attractive, both for large motors and for those requiring wide temperature ranges of operation.
10,965 bytes. 98 x 389 pixels.
Probably the most widely used polybutadiene polymer (1967) had been PBAA, a copolymer of polybutadiene and acrylic acid. One of the added benefits of PBAA over polyurethane was that the binder system was less complex, consisting essentially of the liquid polymer and a single curative chemical such as an epoxide resin. In certain formulations where a large amount of oxidiser and an auxiliary metal-powder fuel such as aluminium was needed to provide high energy, it was necessary to add to the binder a liquid hydrocarbon or other low-viscosity fluid that acted as a plasticiser to aid in processing.
|Titan 401 - Titan 401 - COSPAR 1994-026|
14,308 bytes. 116 x 427 pixels.
By contrast, the polyurethane system normally consisted of a main chain polymer such as a polyether diol, a shorter chain cross-linking agent (perhaps a trifunctional polyol), a curing agent (isocyanate) and a curing catalyst; polyurethanes also employ plasticisers where necessary, usually in the form of aliphatic esters such as dioctyladipate or dioctylsebacate.
Throughout the 1950's propellant manufacturers depended mainly upon rubber chemicals that were readily available to provide the material used in the binders. Among these were PBAA, and the polyethers and polyesters used in polyurethane propellants.
|Ariane 42P V52 - Ariane 42P V52 - COSPAR 1992-052|
13,844 bytes. 108 x 427 pixels.
However, at the beginning of the 1960's the designers of weapon systems appeared to be moving ahead of the propellant manufacturers from the standpoint of operational requirements. Thus it was necessary for the propellant research chemist to visualise the "perfect molecular structure" that would best fulfil the need, and then either make the material or work with a chemical supplier to make it.
The first of these custom-made polymers, pioneered by Phillips Petroleum Co. and first evaluated in propellant applications by Rocketdyne, was carboxy-terminated polybutadiene (CTPB). There was an advantage in placing the carboxyl groups at the end of the polymer chain rather than randomly spacing them along the chain (as PBAA polymers). This way the polymer chemist was provided with a uniform structure so he could control his binder network to give the desired mechanical properties. The reproducibility of a controlled system was naturally greater than that of a random structure.
Credit: Boeing. 21,299 bytes. 367 x 387 pixels.
However, the demand by the customer (primarily the US Government) for greater reliability and overall improved performance suggested that still better binders would be forthcoming. To improve reliability of the CTPB system, for example, a greater insight was needed into the affects of molecular weight and molecular-weight distribution. The influence of molecular structure (isomeric configuration) and minor impurities on mechanical properties was to be determined as part of the continuing research and development.
Credit: Orbital Sciences Corporation. 18,349 bytes. 640 x 196 pixels.
The interplay of mechanical forces between the binder, the aluminium particles, and the ammonium perchlorate crystals would have to be researched until greater knowledge was attained. Information on such fundamentals as energy of wetting, surface free-energy of the solids, the effect of these properties on cracking or other mechanical failure, kinetics of cross-linking reaction, and the effect of temperature and moisture on cure reversion was needed.
There was no doubt that knowledge in these areas would bring about improved hydrocarbon binders.
|PSLV - PSLV - COSPAR 1994-068|
13,953 bytes. 82 x 437 pixels.
PBAN - Polybutadiene Acrylic Acid Acrylonitril Terpolymer (PBAN).
This was the formulation widely used on the 1960-70's big boosters (Titan III & Shuttle).
HTPB - Hydroxyl-Terminated Polybutadiene.
HTPB was the most recent state-of-the-art composite propellant binder, manufactured by ATOChem, Inc. (Boosters: Delta II, Delta III, future Delta IV, Titan IVB and Ariane).
NEW BINDERS TO MEET CLEAN AIR REQUIREMENTS.
Environmental concerns regarding the combustion products of large solid rocket motors used in space launch applications led to a number of 'environmentally friendly' binders being proposed.
|Atlas 2AS - Atlas 2AS - AC-108 - COSPAR 1993-077|
25,075 bytes. 166 x 434 pixels.
GAP: Glycigyl azide polymer, a developmental energetic binder produced by 3M Co. and developed at Valcartier, near Québec, Canada.
Poly-NMMO: Poly-nitratomethyl, methyl oxetane, a developmental energetic binder with a high oxygen content, by Aerojet Solid Propulsion Co.
BTTN: Butanetrioltrinitrate, a highly oxygenated energetic plasticiser.
DMBT: Dimethylbitetrazole, a developmental high nitrogen solid fuel with a high positive heat of formation, used in propellants with oxidisers having high oxygen balances to increase performance, developed at NAWCWPNS.
|Taurus - Taurus - COSPAR 1994-017|
9,939 bytes. 82 x 438 pixels.
Developments Outside of the USA
Other countries begin to study modern composite propellants around mid-1950. Polysulfide remained a nearly an exclusive product of Thiokol. In 1957 design bureau TsKB-7 in the USSR began the study of solid propellants for the D-6 SLBM system, but the technology was not mature. Beginning in 1961 TsKB-7 build the second and the third stages for the Korolev RT-2 ICBM (US code name SS-13 Savage), but the composite propellant technology in USSR remained many years behind that of the west. The RT-2 first flight was in 1966. Beginning in 1961, development began of the RT-15/8K96 mobile IRBM using two stages from the RT-2. The RT-15 would have a range of 4,500 km with a 1.4 tonne payload. However the project was abandoned in 1970 after 19 test launches.
To help provide the high-energy propellants that were required for the more efficient space vehicles and missiles, many propellants used special fuel additives such as powdered metals. Powdered aluminium was used extensively in propellant formulation for the extra energy it contributed and for the help it gave in promoting stable burning. Although powdered beryllium had a higher theoretical energy value than aluminium, it was seldom used because of its extreme toxicity, relative scarcity, and higher cost. In addition, beryllium had a poor combustion efficiency with most of the hydrocarbon binder-fuels available. However, this could be improved by using it with unique and advanced binders like fluorocarbons.
THE SEARCH FOR HIGH ENERGY PROPELLANTS
After WW II, with the Cold War and the prospect of space travel, the search for exotic, energetic fuel was the rule. Boron was the star during the 1950s, but things changed during the 1960s and 1970s. Rocket fuel selection began with an evaluation of the elements from which candidate fuels were, or may be composed. The calculated variation in adiabatic combustion temperature for an oxygen reaction with some of the elements had been reported by Grosse and is reproduced in the table here.
|H-2 - H-2 - COSPAR 1994-007|
21,293 bytes. 121 x 471 pixels.
These temperatures varied considerably and showed that some heavy elements were capable of producing even greater temperatures than light elements such as hydrogen and carbon. However, the heavy elements could quickly be eliminated from consideration (however note that the combustion temperatures would be different with fluorine or other oxidisers). A few, such as zirconium and titanium, were merely competitive on a volumetric heating value basis (BTU/cu ft) and considerably inferior on a gravimetric basis (BTU/lb). Light elements, such as hydrogen, lithium, beryllium, boron, carbon, magnesium and aluminium, appeared interesting.
|Athena-1 - Athena-1 Launch Vehicle|
Credit: Lockheed Martin. 37,942 bytes. 294 x 400 pixels.
Only hydrogen, beryllium and boron had higher heating value than the usual hydrocarbons (HC=~18-19). Beryllium was scarce and extremely toxic, and does not at this time merit serious consideration. High energy fuels, therefore, quickly become restricted to hydrogen and boron and a few classes of compounds containing hydrogen or boron. Special purpose fuels could also involve compounds containing lithium, magnesium, aluminium or carbon. (if one notes that a lighter element goes faster (exhaust velocity) for the same combustion temperature, it can be seen that the carbon and sulphur of black powder, and the sodium in Napalm, were very poor fuels).
Credit: © Mark Wade. 4,873 bytes. 14 x 94 pixels.
EXTOTIC, HIGH ENERGY SOLID PROPELLANTS - THE VIEW IN THE 1960s.
Space and military applications stimulated chemical research so that many exotic and highly reactive ingredients for solid-propellant rockets were produced.
The oxidisers in use consisted of weakly held oxygen atoms in chlorine and nitrogen compounds. It was thought that future oxidisers would have less chlorine and nitrogen atoms, and most of the oxygen would be replaced by fluorine. Some oxygen would remain for the purpose of burning the carbon in the binder to carbon monoxide. Fluorine would be linked to oxygen and nitrogen atoms, with which it forms weak bounds. Nitronium perchlorate and its fluorine derivative (nitronium perfluorate?) were outstanding oxidisers at that time.
|ICBM-Derived LVs - The range of launch vehicles derived from decommissioned ballistic missiles offered for sale by Russia after the cold war.|
Credit: Mark Wade. 41,348 bytes. 640 x 444 pixels.
Fuels would be light-metal hydrides then known, but efforts would be made to replace these by less reactive hydrides of mixed nature. The fuel would be a light-metal hydride with a low heat of formation-one which yields fluorides and oxides with the highest heat of formation. Since rockets using exotic propellants would have a limited volume, the density of the propellant was of critical importance. The best fuels would be light-metal hydrides of low density, a factor which must be considered in the selection of the oxidiser and binder.
Credit: ESA. 11,247 bytes. 196 x 295 pixels.
A major problem was to solve that of preventing the oxidiser and fuel from reacting with each other and with the organic polymeric binder material. Binders would have to be developed which were inert to the fuel and oxidiser. In addition, binders would have to prevent chemical interaction of fuel and oxidiser to avoid possible propellant explosions. The most likely binders would contain long chains of carbon atoms bearing fluorine atoms- (CF2)n -fluorocarbons). The fluorine would serve to consume the fuel and produce inert polymers. These binders would contain little hydrogen since the metal hydrides contained loosely held hydrogen. The performance of these future solid propellants would probably range from 285 to more than 300 seconds. The ultimate solid propellant (specific impulse of up to 350 seconds) would be composed of a binder containing sufficient oxygen to convert its carbon monoxide. A maximum of fluorine-oxygen-carbon groups was also desirable.
|VLS Launch Vehicle - Brazilian VLS space launcher in its launch complex at Alcantara.|
40,022 bytes. 289 x 533 pixels.
Binders more dense than the (CF2)n structure previously mentioned would be difficult to achieve since its density was 50 to 60 percent greater than conventional hydrocarbon binders. In view of compatibility problem with solid propellants, hybrid-propellant systems would have to be developed. Some liquid fuels and oxidisers were superior to their solid counterparts, so the hybrid system should be able to achieve performances which were superior to those of solid propellants.
EXOTIC INGREDIENTS - THE VIEW IN THE 1960s
Credit: ISRC. 7,820 bytes. 98 x 384 pixels.
The development of propellants with higher energy (250-300 Isp) and increased thermal stability (300°F- 500°F) necessitated the incorporation of some exotic chemicals into solid propellants and related devices. Many of these compounds had unusual hazards associated with their uses that were not immediately evident. Others had been used in various phases of research and development and had recognised toxic or explosive properties. The following section lists, with brief comments, some of the more important of these chemicals that were then used in the development of new propellants.
Credit: NASDA. 16,821 bytes. 195 x 330 pixels.
- Nitronium perchlorate or NP (NO2ClO4)-Nitrosyle
- Toxicity- Decomposes above 80°C or in contact with water and many organic compounds. The decomposition of NP releases oxides of nitrogen (NO,NO2) and chlorine (Cl2). Maximum allowable concentration are 5 ppm.
- Sensitivity- Mixtures of NP with nearly all organic compounds are dangerous and explosives and are apt to explode spontaneously. Mixtures with other oxidisable materials behave similarly.
- Uses- Proposed for use in high-energy propellants.
|Delta 3 - Delta 3 on the pad before its first launch attempt.|
Credit: Boeing. 12,783 bytes. 122 x 374 pixels.
- Lithium perchlorate or LP (LiClO4)
Toxicity- Not toxic unless large amounts taken orally.
- Sensitivity- Same as potassium perchlorate. Mixtures with reducing agents are explosives (class B).
- Uses- High-temperature propellants.
- Hydrazinium diperchlorate or HP (N2H6(ClO4)2)
- Toxicity- Decomposes to give chlorine gas (Cl2).
- Sensitivity- Very hazardous material to handle. Extremely
sensitive to impact and friction. Low auto-ignition
- Uses- High-energy propellants.
- Nitrourethanes or NU
Toxicity- All nitro compounds are toxic, some extremely so. Many are absorbed through the skin. Some may cause dermatitis. The alisocyanates from which nitrourethanes are prepared are extremely hazardous.
- Sensitivity- Nitrourethanes are generally class-C explosives, but a few may be more sensitive.
- Uses- High energy propellants.
- Nitramines (HMX, RDX)
Toxicity- Most similar to nitro compounds but more variable, depending on structure. Some may cause severe dermatitis.
- Sensitivity- Some are class-B explosives. Nitrourethanes mixed with this group are generally class C.
- Uses- Experimental only. (1967)
Toxicity- Toxic properties not well established but some are apparently non-toxic.
- Sensitivity- Some propellants and pyrotechnic devices using tetrazoles accidentally exploded, causing several injuries. These devices are regarded as extremely hazardous.
- Uses- Various pyrotechnic devices.(derivatives in high-energy propellants)
- Fluorocarbons or FC
Toxicity- While many FC compounds are completely non-toxic, some are extremely toxic. Pyrolysis of many fluorocarbons may yield gaseous, odourless compounds of extreme toxicity. Kel-F, teflon, and other FC polymers release fluorolefins on heating which among the most toxic of gases. Combustion
of FC propellants release toxic gases (hydrogen fluoride).
- Sensitivity- FC derivatives are not explosive unless mixed with certain powdered metals, metal hydrides, and metallorganic derivatives. These mixtures are not easily exploded by shock, but are exploded by heating.
- Uses- Experimental only.
Toxicity- Many are relatively non-toxic but some of the nitrated or fluorinated materials must be regarded as toxic. Nitrocompounds are absorbed through the skin and cause dermatitis. Dinitriles are toxic; they are absorbed through the skin.
- Sensitivity- All insensitive, except some nitro or nitramino plasticiser.
- Uses- Improved propellants.
Back to Index
Last update 12 March 2001.
Contact Mark Wade with any corrections or comments.
Conditions for use of drawings, pictures, or other materials from this site..
© Mark Wade, 2001 .